| Molecular Principal Chain: | Carbon Chain Polymer |
|---|---|
| Color: | White |
| Feature: | Recycle |
|
Still deciding? Get samples of US$ 12.6/kg
Request Sample
|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
| M.F.I (g/10min) | 4.1~8 | 8.1~12 | 2.1~4 | 0.8~2.0 | 0.8~5.0 | 5.1~10 | 16.1~20 | 20.1~24 | >24 | 12.1~16 |
| Tensile Strength MPa ≥ | 21 | 25 | 27 | Solid % | 50±2 | ≥20 | ≥18 | ≥16 | ≥20 | |
| Elongation at break (%) | 300 | 300 | 320 | Surfactant | 6±1 | ≥300 | 270 | 250 | ≥300 | |
| S.S.G | 2.14~2.17 | (% wt) | 2.14~2.17 | |||||||
| Melting Point (ºC) | 265±10 | PH | 8±1 | 265±10 | ||||||
| Dielectric constant | 2.15 | ------ | ------ | 2.15 | ||||||
| (106HZ)≤ | ||||||||||
| Dielectric loss tangent | 7.0×10-4 | ------ | ------ | 7.0×10-4 | ||||||
| (106HZ) ≤ | ||||||||||
| Volatile (%) ≤ | 0.1 | 0.1 | 0.1 | ------ | ------ | 0.07 | ||||
| Thermal stress-crack resistance | ------ | No crack | No crack | ------ | ------ | ---- | ||||
| Recommend application | Wire and cable, pipe, film, FEP screen and FEP component | Cable, pipe with thin wall thickness | Heat shrinkage tube, lining of pump/Valve/pipe, Cable. | Coating, impregnation of fiber, metal; melted additive of printed-wiring board and so on. | Wire and cable for aerospace, aviation, telecommunication, high building, ele | |||||
| FEP (Fluorinated Ethylene Pro pylene) | |||
| Characteristics: Fine self lubricity, insulation, high temperature resistance, flame retardant, and radiation resistance. | |||
| Application fields: Currently it is mainly applicable to Te flon tube, high temperature electronic wire, RG cable, RF cable,power supply cable, computer control cable, tube and other products, widely used in household appliances, computer, and communication photovoltaic field. | |||
| FEP LC209 Technical Parameter: | |||
| Physical Performance | Specific Gravity |
g/cm3 | 2.12-2.17 |
Melting Flow Rate |
g/10min | 3-5 | |
Melting Point |
ºC | 265±10 | |
| Mechanical Performance | Tensile Strength |
Mpa | >=25 |
Breaking Extension |
% | >=300 | |
Hardness |
Shore hardness |
56 | |
Yield Strength |
Mpa | - | |
Coefficient of dynamic friction |
-- | 0.3 | |
| Thermal Performance | Max imal Temperature of Continuous Work |
ºC | 200 |
| Thermal Distortion Temperature | ºC( 1.82MPa) | 47 | |
| Coefficient of Linear Expansion | (-10-5/ºC) | 8-15 | |
| Electrical Performance | Volume Resistanc | Ω.cm | >1018 |
| Insulation Breakdown Voltage | KV(3.2mm thickness) | 20 | |
| Relative Dielectric Constant | 1KHZ | 2.1 | |
| Dielectric Loss Angle Tangent Value | 1KHZ | <0.0005 | |
| Application fields | large conduct area thick-walled cable insulation and protective jacket, thin pipes, geothermy heating cables | ||
| Extrusion application | Wires over 10AWG, Compound wire protective jacket | ||